堇青石
|
CAPA-CODI | |||
| UNITS | 堇青石 | |||
| 密度 | G/CM3 | 1.8 | ||
| 吸收率 | 15% | |||
| 颜色 | 米白色 | |||
| 特性综述 |
|
|||
| 机械性能 | 维氏硬度 | GPa | - | |
| 弯曲强度 | MOR(20℃) | MPa | 30 | |
| 抗压强度 | MPa | - | ||
| 杨氏模量 | GPa | 140 | ||
| 泊松比 | - | 0.31 | ||
| 断裂韧性 | Mpa・m1/2 | - | ||
| 热性能 | 热膨胀系数 | 40-800℃ | 1x10-6 /℃ | <0.2(22-23℃) |
| 导热性 | 20℃ | W/(m.K) | 2.0 - 3.0 | |
| 比热容 | J/(g.K) | 0.71 | ||
| 耐热冲击性 | ℃ | 1000 | ||
| 电性能 | 介电强度 | kV/mm | - | |
| 体积电阻率 | 20℃ | Ω.cm | >1014 | |
| 300℃ | 1012 | |||
| *以上数值可能会因产品配置和制造过程而有所不同，仅供参考。 | ||||
|
CAPA-Y-ZrO | |||
| UNITS | YTTRIA-STABLIZED ZIRCONIA | |||
| Density | G/CM3 | 6 | ||
| Water Absorption | 0 | |||
| Color | White | |||
| Main Characteristics |
|
|||
| Mechanical Characteristics | Vicker Hardness (Load 500g) | GPa | 12.7 | |
| Flexural Strength | MOR(20℃) | MPa | 1000 | |
| Compressive Strength | MPa | 5000 | ||
| Young's Modulus of Elasticity | GPa | 220 | ||
| Possion Ratio | - | 0.31 | ||
| Fracture Toughness | Mpa・m1/2 | 4 - 5 | ||
| Thermal Characteristics | Coefficient of Linear Thermal Expansion | 40-800℃ | 1x10-6 /℃ | 11.0 |
| Thermal Conductivity | 20℃ | W/(m.K) | 3 | |
| Specific Heat | J/(g.K) | 0.46 | ||
| Heat Shock Resistance(Put in water) | ℃ | - | ||
| Electrical Characteristics | Dielectric Strength | kV/mm | 11.0 | |
| Volume Resistivity | 20℃ | Ω.cm | 1013 | |
| 300℃ | 106 | |||
| *The values are typical material properties and may vary according to products configuration and manufacturing process. | ||||
|
|
CAPA-Mg-ZrO | |||
| UNITS | MAGNESIUM-STABLIZED ZIRCONIA | |||
| Density | G/CM3 | 5.8 | ||
| Water Absorption | 0 | |||
| Color | Beige | |||
| Main Characteristics |
|
|||
| Mechanical Characteristics | Vicker Hardness (Load 500g) | GPa | 12.0 | |
| Flexural Strength | MOR(20℃) | MPa | 545 | |
| Compressive Strength | MPa | 2400 | ||
| Young's Modulus of Elasticity | GPa |
|
||
| Possion Ratio | - |
|
||
| Fracture Toughness | Mpa・m1/2 | 6.0 | ||
| Thermal Characteristics | Coefficient of Linear Thermal Expansion | 40-800℃ | 1x10-6/℃ | 10.2 |
| Thermal Conductivity | 20℃ | W/(m.K) | 2.2 | |
| Specific Heat | J/(g.K) |
|
||
| Heat Shock Resistance(Put in water) | ℃ | - | ||
| Electrical Characteristics | Dielectric Strength | kV/mm |
|
|
| Volume Resistivity | 20℃ | Ω.cm | 1014 | |
| 300℃ |
|
|||
| *The values are typical material properties and may vary according to products configuration and manufacturing process. | ||||
|
|
CAPA-SSiC | |||
| UNITS | SILICON CARBIDE SSIC | |||
| Density | G/CM3 | 3.2 | ||
| Water Absorption | 0 | |||
| Color | Black | |||
| Main Characteristics |
|
|||
| Mechanical Characteristics | Vicker Hardness (Load 500g) | GPa | 23 | |
| Flexural Strength | MOR(20℃) | MPa | 540 | |
| Compressive Strength | MPa | - | ||
| Young's Modulus of Elasticity | GPa | 440 | ||
| Possion Ratio | - | 0.17 | ||
| Fracture Toughness | Mpa・m1/2 | 4 - 5 | ||
| Thermal Characteristics | Coefficient of Linear Thermal Expansion | 40-800℃ | 1x10-6 /℃ | 3.7 - 4.4 |
| Thermal Conductivity | 20℃ | W/(m.K) | 60 | |
| Specific Heat | J/(g.K) | 0.67 | ||
| Heat Shock Resistance(Put in water) | ℃ | - | ||
| Electrical Characteristics | Dielectric Strength | kV/mm | - | |
| Volume Resistivity | 20℃ | Ω.cm | 105 | |
| 300℃ | 104 | |||
| *The values are typical material properties and may vary according to products configuration and manufacturing process. | ||||
|
|
CAPA-RBSiC | |||
| UNITS | REACTION BONDED SILICON CARBIDE | |||
| Density | G/CM3 | 3.2 | ||
| Water Absorption | 0 | |||
| Color | Black | |||
| Main Characteristics |
|
|||
| Mechanical Characteristics | Vicker Hardness (Load 500g) | GPa | 22 | |
| Flexural Strength | MOR(20℃) | MPa | 450 | |
| Compressive Strength | MPa | - | ||
| Young's Modulus of Elasticity | GPa | 430 | ||
| Possion Ratio | - | 0.16 | ||
| Fracture Toughness | Mpa・m1/2 | 4 - 5 | ||
| Thermal Characteristics | Coefficient of Linear Thermal Expansion | 40-800℃ | 1x10-6 /℃ | 3.7 - 4.4 |
| Thermal Conductivity | 20℃ | W/(m.K) | 60 | |
| Specific Heat | J/(g.K) | 0.67 | ||
| Heat Shock Resistance(Put in water) | ℃ | - | ||
| Electrical Characteristics | Dielectric Strength | kV/mm | - | |
| Volume Resistivity | 20℃ | Ω.cm | ||
| 300℃ | ||||
| *The values are typical material properties and may vary according to products configuration and manufacturing process. | ||||
|
|
CAPA-SIN | |||
| UNITS | SILICON NITRIDE | |||
| Density | G/CM3 | 3.2 | ||
| Water Absorption | 0 | |||
| Color | Black | |||
| Main Characteristics |
|
|||
| Mechanical Characteristics | Vicker Hardness (Load 500g) | GPa | 13.9 | |
| Flexural Strength | MOR(20℃) | MPa | 580 | |
| Compressive Strength | MPa | - | ||
| Young's Modulus of Elasticity | GPa | 290 | ||
| Possion Ratio | - | 0.28 | ||
| Fracture Toughness | Mpa・m1/2 | 4 - 5 | ||
| Thermal Characteristics | Coefficient of Linear Thermal Expansion | 40-800℃ | 1x10-6 /℃ | 2.4 - 3.2 |
| Thermal Conductivity | 20℃ | W/(m.K) | 25 | |
| Specific Heat | J/(g.K) | 0.64 | ||
| Heat Shock Resistance(Put in water) | ℃ | - | ||
| Electrical Characteristics | Dielectric Strength | kV/mm | 12 | |
| Volume Resistivity | 20℃ | Ω.cm | >1014 | |
| 300℃ | 1012 | |||
| *The values are typical material properties and may vary according to products configuration and manufacturing process. | ||||
|
|
CAPA-AlN | |||
| UNITS | SILICON NITRIDE | |||
| Density | G/CM3 | 3.2 | ||
| Water Absorption | 0 | |||
| Color | Gray | |||
| Main Characteristics |
|
|||
| Mechanical Characteristics | Vicker Hardness (Load 500g) | GPa | 10.4 | |
| Flexural Strength | MOR(20℃) | MPa | 350 | |
| Compressive Strength | MPa | - | ||
| Young's Modulus of Elasticity | GPa | 310 | ||
| Possion Ratio | - | 0.24 | ||
| Fracture Toughness | Mpa・m1/2 | - | ||
| Thermal Characteristics | Coefficient of Linear Thermal Expansion | 40-800℃ | 1x10-6 /℃ | 4.6 |
| Thermal Conductivity | 20℃ | W/(m.K) | 140 | |
| Specific Heat | J/(g.K) | 0.738 | ||
| Heat Shock Resistance(Put in water) | ℃ | - | ||
| Electrical Characteristics | Dielectric Strength | kV/mm | 25 | |
| Volume Resistivity | 20℃ | Ω.cm | 1012 | |
| 300℃ | ||||
| *The values are typical material properties and may vary according to products configuration and manufacturing process. | ||||
|
|
CAPA-STE | |||
| UNITS | STEATITE | |||
| Density | G/CM3 | 2.8 | ||
| Water Absorption | 0 | |||
| Color | White | |||
| Main Characteristics |
|
|||
| Mechanical Characteristics | Vicker Hardness (Load 500g) | GPa | 5.8 | |
| Flexural Strength | MOR(20℃) | MPa | 140 - 160 | |
| Compressive Strength | MPa | - | ||
| Young's Modulus of Elasticity | GPa | 120 | ||
| Possion Ratio | - | 0.22 | ||
| Fracture Toughness | Mpa・m1/2 | - | ||
| Thermal Characteristics | Coefficient of Linear Thermal Expansion | 40-800℃ | 1x10-6 /℃ | 7.7 - 10.0 |
| Thermal Conductivity | 20℃ | W/(m.K) | 2.0 - 3.0 | |
| Specific Heat | J/(g.K) | |||
| Heat Shock Resistance(Put in water) | ℃ | 250 | ||
| Electrical Characteristics | Dielectric Strength | kV/mm | ||
| Volume Resistivity | 20℃ | Ω.cm | ||
| 300℃ | ||||
| *The values are typical material properties and may vary according to products configuration and manufacturing process. | ||||
|
|
CAPA-CODI | |||
| UNITS | CORDIERITE | |||
| Density | G/CM3 | 2.3 | ||
| Water Absorption | 0 | |||
| Color | Gray | |||
| Main Characteristics |
|
|||
| Mechanical Characteristics | Vicker Hardness (Load 500g) | GPa | - | |
| Flexural Strength | MOR(20℃) | MPa | 30 | |
| Compressive Strength | MPa | - | ||
| Young's Modulus of Elasticity | GPa | 140 | ||
| Possion Ratio | - | 0.31 | ||
| Fracture Toughness | Mpa・m1/2 | - | ||
| Thermal Characteristics | Coefficient of Linear Thermal Expansion | 40-800℃ | 1x10-6 /℃ | <0.2(22-23℃） |
| Thermal Conductivity | 20℃ | W/(m.K) | 2.0 - 3.0 | |
| Specific Heat | J/(g.K) | 0.71 | ||
| Heat Shock Resistance(Put in water) | ℃ | 1000 | ||
| Electrical Characteristics | Dielectric Strength | kV/mm | 19.1 | |
| Volume Resistivity | 20℃ | Ω.cm | >1014 | |
| 300℃ | 1012 | |||
| *The values are typical material properties and may vary according to products configuration and manufacturing process. | ||||